Pengaruh Penambahan Nano Zinc Oxide dan Nano Graphite pada Aluminium Alloy 6061 melalui Proses Pengadukan GesekFriction Stir Processing terhadap Kekerasan Permukaan

Authors

  • Bagas Kurniawan Universitas Muhammadiyah Surakarta
  • Abdul Munir Hidayat Syah Lubis Universitas Muhammadiyah Surakarta
  • Ngafwan Ngafwan Universitas Muhammadiyah Surakarta
  • W. Setiyawan Universitas Muhammadiyah Surakarta
  • Rosy Hilal Mahendra Universitas Gadjah Mada

DOI:

https://doi.org/10.31764/justek.v6i2.14494

Keywords:

Nano Zinc Oxide, Nano Graphite, Friction Stir Processing

Abstract

Abstract:  This study aims to determine whether there is an effect of adding nano zinc oxide and nano graphite to aluminum alloy 6061 through the Friction Stir Processing (FSP) process on surface hardness and wear. The type of research used was quantitative using several tools and materials, namely FSP samples, FSP Chisels, HEM (High Energy Milling) Machines, Sitting Drilling Machines, FSP Machines, Hardness Tester Machines, SEM (Scanning Electron Microscopy) and Optical Microscopes. The results of this study were an increase in hardness after Zn and C application.

Abstrak: Penelitian ini bertujuan untuk mengetahui ada tidaknya pengaruh penambahan nano zinc oxide dan nano graphite pada aluminium alloy 6061 melalui proses Friction Stir Processing (FSP) terhadap kekerasan dan keausan permukaan. Jenis penelitian yang digunakan adalah kuantitatif dengan menggunakan beberapaalat dan bahan yaitu sampel FSP, Pahat FSP, Mesin HEM (High Energy Milling), Mesin Bor Duduk, Mesin FSP, Mesin Hardness Tester, SEM (Scanning Electron Microscopy) dan Mikroskop Optikal. Hasil dari penelitian ini adalah terjadi peningkatan kekerasan setelah pemberian Zn dan C.

References

Arsyad Suyuti, M., . A., Iswar, M., & Nur, R. (2020). Investigasi sifat mekanis sambungan Dissimilar Friction Stir welding (DFSW) Aluminium Alloys (AA5052 to AA6061). Jurnal Energi Dan Manufaktur, 13(2), 49. https://doi.org/10.24843/jem.2020.v13.i02.p01

Assidiq. (2014). Pengaruh Sic Terhadap Sifat Fisis Dan Mekanis Komposit Matrik Aluminium Yang Diperkuat Serbuk Sic. Jurnal Teknik Mesin Undip, 2(3), 211–218.

Cundari, L., Supriyatna, E., & Samhudi, H. (2016). Pengaruh waktu kontak dan kecepatan pengadukan terhadap recovery aluminium pada asidifikasi sludge keluaran water treatment. Jurnal Teknik Kimia, 22(2), 19–27. http://ejournal.ft.unsri.ac.id/index.php/JTK/article/view/881

Handoko, D., Prihantono, T., Setiawan, A., & Mesin, J. T. (2022). Analisa Variasi Putaran Friction Welding Terhadap Kekerasan Logam Aluminium Paduan Seri 1100-H18. 3(2), 15–20. https://doi.org/10.35970/accurate.

Johannes, L. B., Yowell, L. L., Sosa, E., Arepalli, S., & Mishra, R. S. (2006). Survivability of single-walled carbon nanotubes during friction stir processing. Nanotechnology, 17(12), 3081–3084. https://doi.org/10.1088/0957-4484/17/12/044

Jweeg, M. J., Resan, K. K., Abbod, E. A., & Al-Waily, M. (2018). Dissimilar Aluminium Alloys Welding by Friction Stir Processing and Reverse Rotation Friction Stir Processing. IOP Conference Series: Materials Science and Engineering, 454(1). https://doi.org/10.1088/1757-899X/454/1/012059

Lestari, Y., Mabruri, E., Al, P., Pelapisan, O., Steel, S., & Al, N. (2017). Studi Pengaruh Variasi Suhu Perlakuan Panas terhadap Strukturmikro dan Korosifitas pada Pelapisan Ss 410 Menggunakan Komposit Ni-P-Nano Partikel Al2 O3. Jurnal Sains Materi Indonesia, 3.

M. Faizin Alamsyah1, S. (2013). Pengaruh Holding Time Pada Proses Age Hardening Terhadap Kekerasan Komposit Al-Cu Yang Diperkuat Serbuk Fly Ash. Jurnal Teknik Mesin S-1, 1(1), 6–12.

Namdev, A., P., S., Rao, P., O., Bin, M., & Lubis, A., M., H. (2019). Optimization of Friction Stir Process Parameters for Enhancement in Surfece Properties of Al 7075-SiC/Gr Hybrid Surface Composites Coatings, 9, 830; doi:10.3390/coatings9120830

Putra Utama, A. R., Muhayat, N., & Triyono, T. (2019). Pengaruh volume Zn terhadap kekerasan dan struktur mikro pada friction stir processing aluminium AA 1100. Jurnal Teknik Mesin Indonesia, 14(2), 42–46. https://doi.org/10.36289/jtmi.v14i2.129

Rachmatullah, T., Pratikno, H., & Ikhwani, H. (2021). Analisa Pengaruh Variasi Pre-Weld Heat Treatment dan Aging Post Weld Heat Treatment pada Sambungan Las Alumunium 6061 terhadap Kekuatan Tarik dan Struktur Makro. Jurnal Teknik ITS, 9(2), 43–48. https://doi.org/10.12962/j23373539.v9i2.53199

Rahmatika, A., Ibrahim, S., Hersaputri, M., & Aprilia, E. (2019). Studi Pengaruh Variasi Kuat Arus terhadap Sifat Mekanik Hasil Pengelasan GTAW Alumunium 1050 dengan Filler ER 4043. Jurnal Polimesin, 17(1), 47–54.

Rochman, R., Hariyati, P., & Purbo, C. (2010). Karakterisasi Sifat Mekanik dan Pembentukan Fasa Presipitat pada Aluminium Alloy 2024 – T 81 Akibat Perlakuan Penuaan. Mekanika, 8(2), 165–171.

Siswanto, B. D. (2021). Pengaruh Temperatur Artificial Age Terhadap Kekerasan, Kekuatan Luluh dan Kerapatan Dislokasi Pada Paduan Al97,11Mg1,52Si0,86Zn0,51. Journal of Mechanical Engineering Manufactures Materials and Energy, 5(2), 115–133. https://doi.org/10.31289/jmemme.v5i2.4630

Wicaksono, R. T., Suharno, S., & Harjanto, B. (2019). Pengaruh Kuat Arus Pada Pengelasan Paduan Aluminium 6061 Dengan Menggunakan Metode Las Tig Terhadap Kekerasan Dan Struktur Mikro. NOZEL Jurnal Pendidikan Teknik Mesin, 1(1), 37. https://doi.org/10.20961/nozel.v1i1.28484

Zamheri, A. (2011). Pengaruh waktu stirring , fraksi volume, dan ukuran besar butir SiC terhadap kekerasan MMC Al 6061 – SiC dengan sistem stirring casting. Junrnal Austenit, 3(2), 23–34. https://jurnal.polsri.ac.id/index.php/austenit/article/view/125/62

Downloads

Published

2023-06-08

Issue

Section

Articles